The noncovalent immobilization of alkaline phosphatase (ALP) onto aqueous dispersed nylon 6 nanorods ( approximately 310 nm mean diameter; approximately 6 microm mean length) prepared by anodic aluminum oxide (AAO) membrane templating was studied. Using multi-stacked layer-by-layer (LBL) assembly with the cationic quaternary ammonium polymer Sapphire II , the amount of ALP enzyme loaded onto the polymer nanostructures was found to be 115+/-7 microg mg(-1) nanorod. The biofunctionalized nanorods were also characterized for their chemiluminescent activity with the dioxetane substrate, CSPD . The results indicate that the kinetic parameters, K(m) and V(max), for the catalytic activity of the nanostructure-bound ALP enzyme are different from those of soluble ('free') ALP. While the K(m) value was measured to be 156 microM for free ALP, the apparent K(m) value determined for the LBL-immobilized ALP is approximately 20% lower (122 microM). Furthermore, despite the relatively high enzyme loading capacity of the nanorods, the specific activity of the bound ALP enzyme was found to be almost nine times lower than that measured for free ALP. Finally, additional experiments revealed that the catalytic activities of both free ALP and nanorod-conjugated ALP are affected similarly by changes in pH, with optimal performance levels occurring under conditions of pH 9.5. To the best of our knowledge, this study represents the first report examining the preparation of aqueous dispersed, AAO-templated polymer nanorods for potential application as enzyme scaffolds in chemiluminescent-based assay systems.