GaAs nanowires were grown by molecular beam epitaxy and studied by glancing-angle x-ray diffraction during five different stages of the growth process. An entire forest of randomly positioned epitaxial nanowires was sampled simultaneously and a large variation in the Au-Ga catalyst was found. Au, AuGa, AuGa(2) and the hexagonal beta phase were all identified in several orientations and in similar amounts. The nanowires are shown to consist of regular zinc blende crystal, its twin and the hexagonal wurtzite. The evolution of the various Au-Ga catalysts and the development in the twin to the wurtzite abundance ratio indicate that the Au catalyst is saturated upon initiation of growth leading to an increased amount of wurtzite structure in the wires. A specular x-ray scan identifies the various Au-Ga alloys, three Au lattice constants and a rough interface between nanowires and catalyst. Reciprocal space maps were obtained around Au Bragg points and show the development of the Au catalyst from a distribution largely oriented with respect to the lattice to a non-uniform distribution with several well-defined lattice constants.