Until now, polyvinyl alcohol (PVA) gel cylinders have been used in electrolyte diodes as a connecting element between the acidic and alkaline reservoirs. In this paper, a new connecting element is reported: a breath figure templated polyvinyl butyral (PVB) membrane prepared with dip-coating from a dichloromethane solution of the polymer in a humid atmosphere. The procedure gives a 1.5-2 μm thick membrane with a hexagonal pattern, the average characteristic length of which is 1 μm. After an acidic etching, it was found to be a good connecting element. The voltage-current characteristics and dynamic properties of PVA and PVB were measured and compared. The PVB membrane has a faster response to voltage changes than the PVA gel, but in both cases, there was a slow drift in the current that prevented it from reaching a steady state. Reproducible characteristics can be obtained, however, after the current reaches a well-defined quasi-steady state.