The influence of different adherend and substrate materials on shear bond strength (SBS) test was estimated. Ceramic plates (IPS e.max press) were cut, polished, abraded, and applied with two resin cements (Panavia F/Biscem). The SBS values of 30 groups were measured. The groups consisted of five combinations of adherend and substrate materials for each adhesive system and three different bonded areas (2, 4, and 6 mm diameter) for each combination. The failure modes were examined using a stereomicroscope. Groups with ceramic adherends showed higher SBS values in both adhesive systems and all three bonded areas. Small bonded areas are associated with significantly high SBS values. Groups with similar bonded areas and high SBS values showed more mixed or cohesive failures. Groups with small bonded areas and high SBS values had more interfacial failures. Adherend and substrate material significantly influenced the in vitro SBS value.