Nanostructured carbon materials have received considerable attention due to their special physicochemical properties. Herein, ordered mesoporous carbons (OMCs) with two-dimension (2D) hexagonal mesostructure and unique buckled large mesopores have successfully been synthesized via a micelle fusion-aggregation assembly method by using poly(ethylene oxide)-block-polystyrene (PEO-b-PS) diblock copolymers as a template and resorcinol-based phenolic resin as a carbon precursor. The obtained ordered mesoporous carbons possess unique fiber-like morphology, specific surface area of 571-880 m(2)/g, pore volume of 0.54 cm(3)/g and large mesopores (up to 36.3 nm) and high density of active sites (i.e., carboxylic groups) of 0.188/nm(2). Gas sensor based on the ordered mesoporous carbons exhibits an excellent performance in sensing NH3 at a low temperature with fast response (<2 min), ultralow limit of detection (<1 ppm), and good selectivity, due to the large pore sizes, high surface area and rich active sites in the carbon pore walls.