The objective of the study was to investigate alkali lignin polymerization/depolymerization pathways in subcritical water (SW) without additives. Following a SW treatment at 200, 250, 275 and 300 °C, the products were subjected to a comprehensive suite of analyses addressing the product speciation and molecular weight (MW) distribution. The MW reduction (1.4 times) in the solid products following the SW treatment indicated a surprisingly reduced impact of cross-linking/repolymerization at 300 °C and lower temperatures. This was further confirmed by thermal carbon analysis (TCA) showing a reduction in pyrolytic charring after the SW treatment. The TD-Py gas chromatography analysis of the SW treated lignin indicated that the solid residue is less oxygenated than the initial lignin (23 vs. 29% as confirmed by elemental analysis). Thus, deoxygenation rather than re-polymerization appears to be the main process route in the absence of catalysts within the temperature range considered.
Keywords: Gel permeation chromatography; Lignin deoxygenation, lignin valorization; Pyrolysis–gas-chromatography-mass-spectrometry; Thermal carbon analysis.
Copyright © 2021 Elsevier Ltd. All rights reserved.