Nano-sized mesoporous phosphated tin oxide as an efficient solid acid catalyst

S M Hassan; M A Mannaa; Amr Awad Ibrahim

doi:10.1039/c8ra08962k

Nano-sized mesoporous phosphated tin oxide as an efficient solid acid catalyst

RSC Adv. 2019 Jan 8;9(2):810-818. doi: 10.1039/c8ra08962k. eCollection 2019 Jan 2.

Authors

S M Hassan¹, M A Mannaa^{1

2}, Amr Awad Ibrahim^{1

3}

Affiliations

¹ Chemistry Department, Faculty of Science, Mansoura University Mansoura Egypt [email protected].
² Chemistry Department, Faculty of Education and Science, Amran University Sa'dah Yemen.
³ Department of Chemistry, Virginia Commonwealth University Richmond VA 23284-2006 USA.

Abstract

Herein, we prepared a mesoporous tin oxide catalyst (mSnO₂) activated with phosphate species by the adsorption of phosphate ions from a phosphoric acid solution onto tin oxyhydroxide (Sn(OH)₄) surface. The phosphate content ranged from 3 to 45 wt%. The nonaqueous titration of n-butylamine in acetonitrile was used to determine the total surface acidity level. FTIR of chemically adsorbed pyridine was used to differentiate between the Lewis and Brönsted acid sites. Thermal and X-ray diffraction analysis indicated that the addition of phosphate groups stabilized the mesostructure of mSnO₂ and enabled it to keep its crystalline size at the nanoscale. FTIR analysis indicated the polymerization of the HPO₄ ^2- groups into P₂O₇ ^4-, which in turn reacts with SnO₂ to form a SnP₂O₇ layer, which stabilizes the mesoporous structure of SnO₂. The acidity measurements showed that the phosphate species are distributed homogeneously over the mSnO₂ surface until surface saturation coverage at 25 wt% PO₄ ^3-, at which point the acid strength and surface acidity level are maximized. The catalytic activity was tested for the synthesis of hydroquinone diacetate, where it was found that the % yield of hydroquinone diacetate compound increased gradually with the increase in PO₄ ^3- loading on mSnO₂ until it reached a maximum value of 93.2% for the 25% PO₄ ^3-/mSnO₂ catalyst with 100% selectivity and excellent reusability for three consecutive runs with no loss in activity.