The aim of this study was to explain the mechanical differences between EdgeTaper Platinum (ETP) and ProTaper Gold (PTG) determining the transition temperatures and the composition of the alloy of ETP, since no data are present in literature. A total of 130 instruments were selected: 65 ETP F2 and 65 PTG F2. 20 instruments per type were submitted to each mechanical tests. The cyclic fatigue and torsional tests were performed at a pre-set temperature of 35 °C ± 1 °C. During the cyclic fatigue test, Time to fracture, number of cycles to fracture (NCF) and the fragment length (FL) were recorded. During the static torsional, Torque to Fracture (TtF) and FL were recorded. The fracture surface of 5 randomly selected fragments from each test was examined through a Scanning Electron Microscopy (SEM) and an EDX analysis was performed. 20 instruments per type were submitted to a bending test The force generated (grams) to bend each was recorded. Recorded data of mechanical and metallurgical tests were statistically analyzed using a one-way analysis of variance (ANOVA) test with significance set to a 95% confidence level. ETP F2 showed a higher cyclic fatigue resistance and bending ability than PTG F2, with a statistically significant difference (p < 0.05). PTG showed a higher torsional resistance with a statistically significant difference (p < 0.05). DSC analysis of 5 samples for each instrument type pointed out that the austenite finish temperature of PTG was higher than the ETP, respectively of 49.99 ± 3.31 (°C) and 38.92 ± 1.75 (°C). EDX analysis confirmed the near-equiatomic composition of the Ni-Ti alloys, with a presence of a third component recognized as rubidium in the ETP samples. ETP showed higher flexibility in comparison with PTG, despite the latter is characterized by a more martensitic characterization. since its Af temperature is higher than the ETP.
Keywords: NiTi rotary instruments; cyclic fatigue; differential scanning calorimetry; endodontics; flexibility; heat-treatments; torsional resistance.