Theoretical and Experimental Studies of Gallate Melilite Electrides from Topotactic Reduction of Interstitial Oxide Ion Conductors

Lijia Zhou; Jinxiao Zhang; Congling Yin; Luhui Meng; Jiachen Li; Yuexiang Li; Franck Fayon; Mathieu Allix; Xiaojun Kuang

doi:10.1021/acs.inorgchem.2c01393

Theoretical and Experimental Studies of Gallate Melilite Electrides from Topotactic Reduction of Interstitial Oxide Ion Conductors

Inorg Chem. 2022 Jul 18;61(28):10915-10924. doi: 10.1021/acs.inorgchem.2c01393. Epub 2022 Jul 5.

Authors

Lijia Zhou¹, Jinxiao Zhang², Congling Yin¹, Luhui Meng³, Jiachen Li¹, Yuexiang Li³, Franck Fayon⁴, Mathieu Allix⁴, Xiaojun Kuang^{1

2}

Affiliations

¹ MOE Key Laboratory of New Processing Technology for Nonferrous Metal and Materials, Guangxi Key Laboratory of Optic and Electronic Materials and Devices, College of Materials Science and Engineering, Guilin University of Technology, Guilin 541004, P. R. China.
² Guangxi Key Laboratory of Electrochemical and Magneto-chemical Functional Materials, College of Chemistry and Bioengineering, Guilin University of Technology, Guilin 541004, P. R. China.
³ Department of Chemistry, Nanchang University, Nanchang 330031, P. R. China.
⁴ CNRS, CEMHTI UPR3079, Univ. Orléans, F-45071 Orléans, France.

PMID: 35786914
DOI: 10.1021/acs.inorgchem.2c01393

Abstract

A nonstoichiometric La_1.5Sr_0.5Ga₃O_7.25 melilite oxide ion conductor features active interstitial oxygen defects in its pentagonal rings with high mobility. In this study, electron localization function calculated by density functional theory indicated that the interstitial oxide ions located in the pentagonal rings of gallate melilites may be removed and replaced by electron anions that are confined within the pentagonal rings, which would therefore convert the melilite interstitial oxide ion conductor into a zero-dimensional (0D) electride. The more active interstitial oxide ions, compared to the framework oxide ions, make the La_1.5Sr_0.5Ga₃O_7.25 melilite structure more reducible by CaH₂ using topotactic reduction, in contrast to the hardly reducible nature of parent LaSrGa₃O₇. The topotactic reduction enhances the bulk electronic conduction (σ ∼ 0.003 S/cm at 400 °C) by ∼ 1 order of magnitude for La_1.5Sr_0.5Ga₃O_7.25. The oxygen loss in the melilite structure was verified and most likely took place on the active interstitial oxide ions. The identified confinement space for electronic anions in melilite interstitial oxide ion conductors presented here provides a strategy to access inorganic electrides from interstitial oxide ion conductor electrolytes.