Tribological Properties of a Sliding Joint with an a-C:H:W Coating under Lubrication Conditions with PAO8 Oil and the Addition of 2% MoS₂ Nanoparticles

One of the promising methods for improving the durability and reliability of friction joints in combustion engines is the use of thin and hard coatings, including coatings based on amorphous DLC. The a-C:H:W coating was produced using the commercial PVD method. The tested tribological joints were made of AISI 4337 steel and SAE-48 bearing alloy (conformal contact) and AISI 4337 steel and valve shims (non-conformal contact). The contact area was lubricated with SAE 5W40 engine oil and PAO8 oil + 2 wt.% MoS₂ nanoparticles. The objective of this work is to explore the influence of PAO8 + MoS₂ on the tribological properties of a sliding joint with an a-C:H:W coating and the change in the properties of the oils. In the conformal contact, the lubrication of the a-C:H:W coating with PAO8 + MoS₂ caused a significant increase in the friction resistance (than in) as compared to the joints with a quenching and tempering surface layer and lubricated SAE 5W40, while in the non-conformal contact, the lubrication of the a-C:H:W coating with PAO8 + MoS₂ caused a decrease in the friction resistance and temperature of the contact area. The joints with the a-C:H:W coating were characterized by higher wear of the SAE-48 bearing alloy, as compared to the joints with the surface layer without coating (lubricated with SAE 5W40 oil-11-fold increase, PAO8 + MoS₂-46-fold increase). The wear of valve shims with the a-C:H:W coating was significantly lower as compared to the wear of the commercial version of the valve shims (the difference between joints lubricated with SAE 5W40 oil and PAO8 + MoS₂ was 12%, 36% and 29% for unit pressures of 10, 15 and 20 MPa). Lubrication of the a-C:H:W coating with PAO8 oil + MoS₂ protected the sliding joints against seizing in non-conformal contact.