Impact of morphology and oxygen vacancy content in Ni, Fe co-doped ceria for efficient electrocatalyst based water splitting

Abhaya Kumar Mishra; Joshua Willoughby; Shanna L Estes; Keliann Cleary Kohler; Kyle S Brinkman

doi:10.1039/d4na00500g

Impact of morphology and oxygen vacancy content in Ni, Fe co-doped ceria for efficient electrocatalyst based water splitting

Nanoscale Adv. 2024 Jul 23;6(18):4672-4682. doi: 10.1039/d4na00500g. eCollection 2024 Sep 10.

Authors

Abhaya Kumar Mishra¹, Joshua Willoughby¹, Shanna L Estes², Keliann Cleary Kohler³, Kyle S Brinkman¹

Affiliations

¹ Department of Materials Science and Engineering, Clemson University Clemson SC 29634 USA [email protected].
² Department of Environmental Engineering and Earth Sciences, Clemson University Anderson SC 29625 USA [email protected].
³ Advanced Materials Research Laboratory (AMRL), Clemson University Anderson SC 29625 USA [email protected].

Abstract

Designing a highly efficient, low-cost, sustainable electrocatalyst for the hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) through water splitting is a current challenge for renewable energy technologies. This work presents a modified sol-gel route to prepare metal-ion(s) doped cerium oxide nanostructures as an efficient electrocatalyst for overall water splitting. Nickle (Ni) and iron (Fe) co-doping impacts the morphology in cerium oxide resulting in 5 nm nanoparticles with a mesoporous-like microstructure. The high level 20 mol% (1 : 1 ratio) of Ni + Fe bimetal-ion(s) doped CeO₂ shows excellent HER and OER activities compared to the monodoped Fe/Ni and pristine CeO₂. The co-doped catalysts required a low overpotential of 104 mV and 380 mV for HER and OER, respectively, in 1 M KOH, at a current density of 10 mA cm^-2. The Tafel slopes of 95 mV dec^-1 and 65 mV dec^-1 were measured for HER and OER with the same representative samples which demonstrated excellent stability even after continuous operation for 20 hours in the alkaline medium. The unique morphology, enhanced oxygen vacancy (O_v) content and the synergistic effects of dopants in CeO₂ play essential roles in enhancing the activities of Ni + Fe doped samples.