Low-Cycle Fatigue Damage Mechanism and Life Prediction of High-Strength Compacted Graphite Cast Iron at Different Temperatures

Tensile and low-cycle fatigue tests of high-strength compacted graphite cast iron (CGI, RuT450) were carried out at 25 °C, 400 °C, and 500 °C, respectively. The results show that with the increase in temperature, the tensile strength decreases slowly and then decreases rapidly. The fatigue life decreases, and the life reduction increases at high temperature and high strain amplitude. The oxide layer appears around the graphite and cracks at high temperature, and the dependence of crack propagation on ferrite gradually decreases. With the increase in strain amplitude, the initial cyclic stress of compacted graphite cast iron increases at three temperatures, and the cyclic hardening phenomenon is obvious. The fatigue life prediction method based on the energy method and damage mechanism for compacted graphite cast iron is summarized and proposed after comparing and analyzing a large amount of fatigue data.