Molecular dynamics study of mechanical stability of Ti₄C₃ MXene subjected to chirality, temperature, strain rate, and point-vacancy for Lithium-ion batteries

Two-dimensional Ti₄C₃ MXene has recently emerged as a promising electrode for Lithium-ion batteries (LIBs) because of its outstanding ion-transport abilities and high Li-absorbability. This study employed molecular dynamics simulation to explore the mechanical stability of Ti₄C₃ MXene subjected to various temperatures, strain rates, and vacancy concentrations. A slightly superior tensile strength and elasticity modulus have been observed along zigzag directions, measuring 148.14 GPa and 29.17 GPa, respectively. On the other hand, armchair-oriented Ti₄C₃ MXene shows a considerably greater fracture strain of 0.259 due to its strain-hardening tendency at lower temperatures. Elevated temperature decreases both fracture strength and fracture strain, which is opposite to the effect of strain rate. Armchair loading has been revealed to be more sensitive to strain rate than its counter direction. Unlike temperature and strain rate, point vacancy significantly deteriorates the elastic modulus of Ti₄C₃ MXene. Carbon vacancies are more probable than titanium vacancies, which have less formation energy. The atomistic deformation profile supports the predicted values of fracture strain from stress-strain behavior. This in-depth study offers a detailed understanding of the mechanical behavior of Ti₄C₃ MXene under diverse circumstances, which will aid further experimental study and be beneficial for adopting Ti₄C₃ as anode materials in LIBs.