Fast, Highly Stable, and Low-Bandgap 2D Halide Perovskite Photodetectors Based on Short-Chained Fluorinated Piperidinium as a Spacer

Norman Lu; Gurumallappa Gurumallappa; Jitendra Singh; Ka Long Chan; Eskedar Tessema; Pin-Yu Liu; Hema Mylnahalli Krishnegowda; Karthik Chimatahalli Shanthakumar; Jinn-Hsuan Ho; Yu-Chiang Chao; Lam-Gia-Hao Dao; Sumedh Shirsat; Meng-Lin Tsai

doi:10.1021/acsami.4c18202

Fast, Highly Stable, and Low-Bandgap 2D Halide Perovskite Photodetectors Based on Short-Chained Fluorinated Piperidinium as a Spacer

ACS Appl Mater Interfaces. 2024 Dec 16. doi: 10.1021/acsami.4c18202. Online ahead of print.

Authors

Affiliations

¹ Institute of Organic and Polymeric Materials, National Taipei University of Technology, Taipei 106, Taiwan.
² Graduate Institute of Energy and Optoelectronic Materials National Taipei University of Technology, Taipei 106, Taiwan (ROC).
³ Department of Physics, Udit Narayan Post Graduate College Padrauna Kushinagar, affiliated by Deen Dayal Upadhyaya Gorakhpur University, Kushinagar 274304, Uttar Pradesh, India.
⁴ Department of Chemistry, SJCE, JSS Science and Technology University, Mysuru 570 006, Karnataka, India.
⁵ Department of Chemical Engineering, National Taiwan University of Science and Technology, Taipei 106335, Taiwan.
⁶ Department of Physics, National Taiwan Normal University, Taipei 106, Taiwan.
⁷ Department of Materials Science and Engineering, National Taiwan University of Science and Technology, Taipei 106335, Taiwan.

PMID: 39681536
DOI: 10.1021/acsami.4c18202

Abstract

Ruddlesden-Popper (RP) two-dimensional (2D) halide perovskite (HP), with attractive structural and optoelectronic properties, has shown great potential in optoelectrical devices. However, the relatively wide bandgap (E_g) and stability, which cause inferior efficiency, prevent its feasibility from further applications. To tackle these issues, for the first time, a novel fluorine-containing piperidinium spacer, (3-HCF₂CF₂CH₂OCH₂-PPH⁺), abbreviated as (4FH-PPH⁺), has been designed for the stable and efficient n = 1 2D HPs. Its fluorophobicity can significantly enhance the noncovalent interactions between cations and [PbI₆]^4- octahedra. The observed E_g of the fluorinated (4FH-PPH)₂PbI₄ perovskite is found to be 2.22 eV, which is the lowest value among all fluorinated perovskites reported so far. Interestingly, this fluorinated film-based 2D perovskite photodetector (PD) exhibits the outstanding responsivity of 502 mA W^-1, photodetectivity of 5.73 × 10¹⁰ cm Hz^1/2 W^-1, and impressive response/recovery time of 42/46 ms under 450 nm at 20 V. To the best of our knowledge, it is found for the first time that the 2D HP, with the fluorinated short-chained segment included into the organic spacer, shows remarkable stability for up to 49 days. These results strongly demonstrate the potential of the 2D fluorinated short-chained (4FH-PPH)₂PbI₄ HP with a low E_g as a promising candidate for next-generation optoelectronic devices.

Keywords: (2D halide perovskite; fluorinated photodetector; fluorinated piperidinium organic spacer); noncovalent interactions (NCIs); tunable energy bandgap.