Formation of well-aligned ZnGa(2)O(4) nanowires from Ga(2)O(3)/ZnO core-shell nanowires via a Ga(2)O(3)/ZnGa(2)O(4) epitaxial relationship

Ko-Wei Chang; Jih-Jen Wu

doi:10.1021/jp051925+

Formation of well-aligned ZnGa(2)O(4) nanowires from Ga(2)O(3)/ZnO core-shell nanowires via a Ga(2)O(3)/ZnGa(2)O(4) epitaxial relationship

J Phys Chem B. 2005 Jul 21;109(28):13572-7. doi: 10.1021/jp051925+.

Authors

Ko-Wei Chang¹, Jih-Jen Wu

Affiliation

¹ Department of Chemical Engineering, National Cheng Kung University, Tainan, Taiwan.

PMID: 16852699
DOI: 10.1021/jp051925+

Abstract

Formation of well-aligned and single-crystalline ZnGa(2)O(4) nanowires on sapphire (0001) substrates has been achieved via annealing of the Ga(2)O(3)/ZnO core-shell nanowires. Ga(2)O(3)/ZnO core-shell nanowires were prepared using a two-step method. The thickness of the original ZnO shell and the thermal budget of the annealing process play crucial roles for preparing single-crystalline ZnGa(2)O(4) nanowires. Structural analyses of the annealed nanowires reveal the existence of an epitaxial relationship between ZnGa(2)O(4) and Ga(2)O(3) phases during the solid-state reaction. A strong CL emission band centered at 360 nm and a small tail at 680 nm are obtained at room temperature from the single-crystalline ZnGa(2)O(4) nanowires.