This study aimed to evaluate the influence of fluoride-containing mouthrinse solutions (Fluorgard and Oral B) on the superficial microhardness of two resin-modified glass ionomer cements (Vitremer and Fuji II LC). Fifteen discs-shaped specimens of each glass ionomer cement (Ø10 mm; 2 mm thick) were prepared, thereby forming two groups. After 24-hour storage in artificial saliva, the microhardness was measure and the data were recorded. Next, each group was divided into three subgroups (n = 5), according to the solution to be immersed in. Control specimens were kept in artificial saliva along the whole experiment. The test specimens were kept in mouthrinse solution for 30 days. Vickers surface microhardness was analyzed at predetermined evaluation periods: 24 h, 48 h, 7, 14, 21 and 30 days after specimens' preparation. Data were subjected to three-way ANOVA and to Tukey test (p<0.05). A better behavior of Fuji II LC was observed and Fluorgard affected most the characteristics of the tested materials. It may be concluded that fluoride-containing solutions influenced the tested characteristics of materials, mainly of Vitremer.