Uniform Gd2O3 : Eu3+ nanowires were fabricated by using anodic aluminum oxide template (AAO). The spectral measurements indicate that with the increasing annealing temperature the excitation band of Eu3+ in Gd2O3 : Eu3+ nanowires/AAO shifted blue, the intensity ratio of 5D0-7F2 to 5D0-7F1, decreased, and the lifetime became longer. In the sample annealed at 1000 degrees C two spectral components, the sharper and broader lines were identified, corresponding to two different local environments, the Eu3+ ions in cubic phase and in amorphous phase, respectively. The 5D0-7F1 transitions of Eu3+ ions in cubic phase had longer lifetime than that in amorphous phase. In contrast to the lifetime of the 5D0-7F(j) transitions in the bulk, that in Gd2O3 : Eu3+/AAO composite films increased due to influence of the surrounding media (AAO).