The influence of Al(2)O(3) nanoparticles on the curing of an epoxy thermoset based on diglycidyl ether of bisphenol A was investigated using temperature-modulated differential scanning calorimetry (TMDSC) and rheology. Diethylene triamine was used as a hardener. TMDSC not only allows for a systematic study of the kinetics of cure but simultaneously gives access to the evolution of the specific heat capacities of the thermosets. The technique thus provides insight into the glass transition behaviour of the nanocomposites and hence makes it possible to shed some light on the interaction between the nanoparticles and the polymer matrix. The Al(2)O(3) fillers are shown to accelerate the growth of macromolecules upon isothermal curing. Several mechanisms which possibly could be responsible for the acceleration are described. As a result of the faster network growth chemical vitrification occurs at earlier times in the filled thermosets and the specific reaction heat decreases with increasing nanoparticle concentration. Rheologic measurements of the zero-shear viscosity confirm the faster growth of the macromolecules in the presence of the nanoparticles.