New compound discovery is of interest in the field of inorganic solid-state chemistry. In this work, a whitlockite-type structure Sr1.75Ca1.25(PO4)2 newly found by composition design in the Sr3(PO4)2-Ca3(PO4)2 join was reported. Crystal structure and luminescence properties of Sr1.75Ca1.25(PO4)2:Eu(2+) were investigated, and the yellow-emitting phosphor was further employed in fabricating near-ultraviolet-pumped white light-emitting diodes (w-LEDs). The structure and crystallographic site occupancy of Eu(2+) in the host were identified via X-ray powder diffraction refinement using Rietveld method. The Sr1.75Ca1.25(PO4)2:Eu(2+) phosphors absorb in the UV-vis spectral region of 250-430 nm and exhibit an intense asymmetric broadband emission peaking at 518 nm under λex = 365 nm which is ascribed to the 5d-4f allowed transition of Eu(2+). The luminescence properties and mechanism are also investigated as a function of Eu(2+) concentration. A white LED device which is obtained by combining a 370 nm UV chip with commercial blue phosphor and the present yellow phosphor has been fabricated and exhibit good application properties.