CsTlCl(3) and CsTlF(3) perovskites have been theoretically predicted to be superconductors when properly hole-doped. Both compounds have been previously prepared as pure compounds: CsTlCl(3) in a tetragonal (I4/m) and a cubic (Fm3̅m) perovskite polymorph and CsTlF(3) as a cubic perovskite (Fm3̅m). In this work, substitution of Tl in CsTlCl(3) with Hg is reported, in an attempt to hole-dope the system and induce superconductivity. The whole series CsTl(1-x)HgxCl(3) (x = 0.0, 0.1, 0.2, 0.4, 0.6, and 0.8) was prepared. CsTl(0.9)Hg(0.1)Cl(3) is tetragonal as the more stable phase of CsTlCl(3). However, CsTl(0.8)Hg(0.2)Cl(3) is already cubic with the space group Fm3̅m and with two different positions for Tl(+) and Tl(3+). For x = 0.4 and 0.5, solid solutions could not be formed. For x ≥ 0.6, the samples are primitive cubic perovskites with one crystallographic position for Tl(+), Tl(3+), and Hg(2+). All of the samples formed are insulating, and there is no signature of superconductivity. X-ray absorption spectroscopy indicates that all of the samples have a mixed-valence state of Tl(+) and Tl(3+). Raman spectroscopy shows the presence of the active Tl-Cl-Tl stretching mode over the whole series and the intensity of the Tl-Cl-Hg mode increases with increasing Hg content. First-principle calculations confirmed that the phases are insulators in their ground state and that Hg is not a good dopant in the search for superconductivity in this system.