The SnO₂/g-C₃N₄ composites were synthesized via a facile calcination method by using SnCl₄·5H₂O and urea as the precursor. The structure and morphology of the as-synthesized composites were characterized by the techniques of X-ray diffraction (XRD), the field-emission scanning electron microscopy and transmission electron microscopy (FESEM and TEM), energy dispersive spectrometry (EDS), thermal gravity and differential thermal analysis (TG-DTA), and N₂-sorption. The analysis results indicated that the as-synthesized samples possess the two dimensional structure. Additionally, the SnO₂ nanoparticles were highly dispersed on the surface of the g-C₃N₄ nanosheets. The gas-sensing performance of the as-synthesized composites for different gases was tested. Moreover, the composite with 7 wt % g-C₃N₄ content (SnO₂/g-C₃N₄-7) exhibits an admirable gas-sensing property to ethanol, which possesses a higher response and better selectivity than that of the pure SnO2-based sensor. The high surface area of the SnO2/g-C3N4 composite and the good electronic characteristics of the two dimensional graphitic carbon nitride are in favor of the elevated gas-sensing property.
Keywords: SnO2; SnO2/g-C3N4 composite; calcination method; ethanol gas sensing; graphitic carbon nitride.