Novel graphene-oxide-reinforced silicone composites (GOSC) are prepared by in situ polymerization of silanes and low concentrations (<0.15 wt%) of silylated GO (SGO). After modification, the distances of the SGO nanosheets are successfully increased from 0.72 to 0.87 nm. Compared with GO, the SGO shows better dispersibility in organic solvents as well as remarkably enhanced decomposition temperature (T d improved by 100 °C). After covalently grafting onto silicone resins via in situ polymerization, the obtained GOSC exhibits greatly enhanced thermal stability (T d up to 400 °C and T g improved by 3-5 °C), increased storage modulus, loss modulus, and complex viscosity. The morphology, microstructure, interfacial adhesion of the developed GOSC coatings were carefully investigated. The GOSC coatings on metal exhibit good transparency (up to 90%), hydrophobicity, and excellent anticorrosion capability. This work provides a new strategy for developing high performance graphene-based silicone composite materials.
Keywords: anticorrosion; graphene oxide; in situ polymerization; silicone matrix; silylation.
© 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.