Correlation of Time-Dependent Oxygen Surface Exchange Kinetics with Surface Chemistry of La_0.6Sr_0.4Co_0.2Fe_0.8O_3-δ Catalysts

The Sr segregation at the surface of a perovskite La_0.6Sr_0.4Co_0.2Fe_0.8O_3-δ (LSCF) oxygen electrode is detrimental to the electrochemical performance and durability of energy conversion devices such as solid oxide fuel cells. However, a quantitative correlation of degradation of the oxygen surface exchange kinetics with Sr precipitation formation at the LSCF surface is not clearly understood yet. Herein, the correlation of the time-dependent degradation mechanisms of the LSCF catalysts with respect to Sr segregation phenomenon at the surface were investigated at 800 °C for a prolonged annealing time (∼800 h) by combining in situ electrochemical measurements, and ex situ chemical and structural analyses at the multiscale. The in situ monitored surface exchange coefficient (k_chem) was found to drastically drop by ∼86% over the 800 h, and it was accompanied by the formation of Sr-containing secondary phases on the bulk LSCF surface, as expected. However, the estimated coverage of Sr segregation on the LSCF surface was only ∼15%, even after 800 h of aging time, showing significant deviation from the k_chem degradation rate (∼86%). The surface chemistry evolution at the clean surface area, which is believed to be electrochemically active, was further analyzed on the nanoscale. The quantified results showed that the Sr elemental fraction of the A-site at the outermost surface of the LSCF samples was becoming deficient from ∼4.0 at 0 h to ∼0.27 at 800 h annealing. Interestingly, the time-dependent behavioral tendencies between k_chem degradation and surface Sr fractional changes were highly analogous. Thus, our results suggest that this Sr deficiency at the clean surface region more dominantly impacts the degradation process rather than an electrochemical activity passivation by the SrO_x precipitates, which has been shown to be a major degradation mechanism of LSCF performance.