Low-dimensional quantum materials that remain strongly ferromagnetic down to monolayer thickness are highly desired for spintronic applications. Although oxide materials are important candidates for the next generation of spintronics, ferromagnetism decays severely when the thickness is scaled to the nanometer regime, leading to deterioration of device performance. Here, a methodology is reported for maintaining strong ferromagnetism in insulating LaCoO3 (LCO) layers down to the thickness of a single unit cell. It is found that the magnetic and electronic states of LCO are linked intimately to the structural parameters of adjacent "breathing lattice" SrCuO2 (SCO). As the dimensionality of SCO is reduced, the lattice constant elongates over 10% along the growth direction, leading to a significant distortion of the CoO6 octahedra, and promoting a higher spin state and long-range spin ordering. For atomically thin LCO layers, surprisingly large magnetic moment (0.5 μB /Co) and Curie temperature (75 K), values larger than previously reported for any monolayer oxides are observed. The results demonstrate a strategy for creating ultrathin ferromagnetic oxides by exploiting atomic heterointerface engineering, confinement-driven structural transformation, and spin-lattice entanglement in strongly correlated materials.
Keywords: complex oxide superlattices; ferromagnetism; polarized neutron reflectometry; spintronics.
© 2020 Wiley-VCH GmbH.