Silver-hydroxyapatite nanocomposites prepared by three sequential reaction steps in one pot and their bioactivities in vitro

Hydroxyapatite (HA) combined with antimicrobial agents for biomedical application can effectively avoid the bacteria infection, while HA have the good performance. In this study, we prepared silver-hydroxyapatite (Ag-HA) nanocomposites using a one-pot method consisting of three sequential steps of wet chemical precipitation, ion exchange, and a silver mirror reaction. The HA nanoparticles used as the precursor for Ag ion doping were first synthesised by wet chemical precipitation. Next, Ag⁺ absorbed on HA surface through ion exchange reaction. Glucose was then added to initiate the silver mirror reaction, which made the Ag⁺ ions reduce to Ag⁰ and Ag nanoparticles in situ formed on HA nanoparticles. Subsequently, Ag-HA nanocomposites with different Ag content were prepared. X-ray diffraction, SEM, EDX mapping and TEM imaging confirmed that spherical Ag nanoparticles ~20-40 nm in diameter were adhered to the surface of HA nano-rods (0.4-0.8 μm in length and 15-40 nm in diameter). The Ag content (1.9-15.2 wt%) in the Ag-HA nanocomposites was adjusted by varying the feeding Ag/Ca molar ratio (2.0-20%). The cell viability evaluation in vitro proved that Ag-HA nanocomposites had low cytotoxicity to L929 normal cells. Meanwhile, the antibacterial examinations in vitro demonstrated that Ag-HA nanocomposites had obvious antibacterial effects on Gram-positive bacteria, Gram-negative bacteria, and fungus. The antibacterial results were dose-dependent on the accumulation of silver content. The Ag-HA nanocomposites loaded PMMA resins also demonstrated a potential antibacterial activity against S. mutans. This paper presents a convenient and bio-friendly approach for preparing Ag-HA nanocomposites with adjustable Ag content, which are a promising material for biomedical applications.