Achieving Electronic Engineering of Vanadium Oxide-Based 3D Lithiophilic Sandwiched-Aerogel Framework for Ultrastable Lithium Metal Batteries

ACS Appl Mater Interfaces. 2022 Jul 13. doi: 10.1021/acsami.2c08117. Online ahead of print.

Abstract

Lithium (Li) metal is one of the most promising anode materials for the next-generation batteries, which owns superior specific capacity and energy density. Unfortunately, lithium dendrites that is formed during the charging/discharging process tends to induce capacity degradation and thus short lifespan. In this study, the vanadium oxide (V2O5) and nitrogen-doped vanadium oxide (N-V2O3, N-VO0.9)-modified three-dimensional (3D) reduced graphene oxide ((N)-VOx@rGO) with tunable electronic properties are demonstrated to enable the dendrite-free Li deposition. The soft lithiophilic rGO as the scaffold can provide sufficient void space for Li storage. Meanwhile, the rigid (N)-VOx uniformly anchored on rGO can perfectly maintain the 3D structure, which is crucial for Li to enter the inner space of the 3D framework. Consequently, the (N)-VOx@rGO electrodes achieve dendrite-free electrodeposition under the multifarious deposition capacity and current densities. Compared with the bare lithium electrodes, the asymmetrical cells of (N)-VOx@rGO anode can cycle stably up to 400 h at 2 mA cm-2 current density, together with a low nucleation overpotential of ∼20 mV.

Keywords: 3D framework; electronic engineering; lithium metal battery; reduced graphene oxide; vanadium oxide.