Photocatalytic activity of P-doped TiO₂ photocatalyst

In this study, P-doped TiO₂ photocatalysts with different molar percentages (in the range 0.071-1.25 mol %) of the non-metallic element were prepared and their photocatalytic activity under visible light irradiation was tested. All achieved samples were characterized by XRD, Raman, UV-Vis DRS and SEM-EDX techniques. XRD and Raman analysis showed that all doped photocatalysts were in anatase phase and evidenced that P ions were successfully incorporated into the TiO₂ crystal lattice, affecting also the crystallinity degree of the P-doped TiO₂ photocatalysts. Noticeably, the UV-Vis DRS spectra evidenced that the highest redshift in absorption edge was observed for the photocatalyst with the lowest P content (0.071PT), which showed also the lowest bandgap (2.9 eV). The photocatalytic performances of all P-doped TiO₂ samples were compared with that of commercial TiO₂ by evaluating the decolorization of methylene blue (MB) dye under visible light irradiation. Results showed that phosphorus doping strongly promoted photocatalytic activity in the presence of visible light. Furthermore, the most active photocatalyst in visible light tests (0.071PT) also showed better photocatalytic activity than commercial TiO₂ in the decolorization of MB under simulated sunlight irradiation. Finally, 0.071PT photocatalyst was preliminarily tested against Escherichia coli (E. coli) under simulated solar light, showing an inactivation efficiency of 90% after 2 h of treatment time.