Gingerol and Chitosan-Based Coating of Thermoformed Orthodontic Aligners: Characterization, Assessment of Anti-Microbial Activity, and Scratch Resistance: An In Vitro Study

Aim To prepare and characterize a 6-gingerol-incorporated chitosan biopolymer for coating on thermoformed aligners and evaluate its scratch resistance and antimicrobial activity. Material and methods In this in vitro study, 6-gingerol extract was prepared, incorporated with chitosan biopolymer into a coating solution and characterized using nuclear magnetic resonance imaging spectroscopy (NMR). Twenty thermoformed aligner samples were exposed to UV radiation for surface activation, then coated with a crosslinking agent. These were divided into four groups of five. The control group consisted of samples dip-coated in a chitosan solution for 15 minutes. The three test groups consisted of samples dip coated in a gingerol-chitosan coating solution, with each group representing the following time periods of dip coating: five, 10, and 15 minutes. The crosslinking of the coating with the aligner material was confirmed by a Fourier transform infrared spectroscopy (FTIR) test. A scratch test was carried out to evaluate the wear resistance of the coating, and the antibacterial properties of the coating were tested using a Disc Diffusion test. Results The NMR analysis confirmed the presence of 6-gingerol in the extract. The coating of 6-Gingerol on aligners was confirmed by FTIR spectroscopy. The wear resistance of aligners coated for 5 minutes, 10 minutes, and 15 minutes was 1.8 ± 0.09 N, 2.3 ± 0.021 N, and 3.06 ± 0.17 N, respectively, and the difference was statistically significant (p<0.05). The aligner coated for 15 minutes exhibited the widest zone of inhibition of up to 2.38 ± 0.44 mm against Streptococcus mutans, and the difference was statistically significant (p<0.05).​​​​​​ No antibacterial effect was found against E. Coli. Conclusion A novel coating material with 6-gingerol extract incorporated in chitosan biopolymer was prepared and characterized, followed by coating on thermoformed aligners. The coating showed antibacterial activity against Streptococcus mutans, and both the antimicrobial activity and wear resistance increased with coating duration.