This novel research addresses the critical need for sustainable and efficient materials, aiming to enhance the optical and thermoelectric properties of Aluminum doped Zinc Oxide (Al-doped ZnO) on cellulose fabric for diverse applications. At first stage, Cellulosic fabric of Al-doped ZnO were experimentally studied in detail with respect to varying levels of annealing temperature. Structural analysis unveiled structural evolution in hexagonal crystal formations with a reduction in particle size up to 27.5 % on average, with increased temperature. Further, Raman spectroscopy revealed the doping effects on the vibrational modes of ZnO, potentially due to alterations in lattice structure. The ZnO optical modes are found as E2 (low) = 110 cm-1 with observed phonon frequency in the Raman spectra of ZnO at A1 (TO) = 364 cm-1. Fourier transform infrared spectroscopy (FTIR) revealed the presence of characteristic stretching of developed material. Furthermore, the optical characters revealed a decrement of 43.22 % in bandgap values with increasing annealing temperature. The analysis of thermoelectric attributes documented that the prominent sample annealed at 300°C exhibited the maximum Seebeck coefficient and power factor of 2.1 × 10-3 μV/oC and 5.8 × 10-21 Wm-1 K-2, respectively. At second stage the optical characteristics of experimentally optimized sample were rigorously studied through the application of Material Studio software, while varying the doping ratio.
Keywords: Conductive textiles; Thermal evaporation; Thermoelectric.
Copyright © 2024 Elsevier B.V. All rights reserved.