Multifunctional and Hierarchical Porous ZIF-8: Amine and Thiol Tagged via Mixed Multivariate Ligand Strategies for Enhanced CO2 and Iodine Adsorption

This study demonstrated a simple and innovative way of using the direct de novo synthesis to fabricate the mesoporous structure and diverse functionality of ZIF-8 for environmental cleanup and gas storage applications. By introducing different ligands, we have developed a version of ZIF-8 that could better capture carbon dioxide (CO2) and iodine. The ZIF-8 was successfully designed to have the hierarchical and mesoporous structure with the functional groups of amine and thiol groups by adjusting the pKa values (from 8 to 12) of ligand instead of original ligand, 2-methyl imidazole (Hmim, pKa~14.2). The modulation of ZIF-8 particle size, porosity, and functional characteristics was achieved through varied ligands and their concentrations, streamlined into a single and room-temperature synthesis condition. The resulting ZIF-8 materials exhibit intricate hierarchical architectures and a high density of functional groups, significantly enhancing molecular diffusion and accessibility. Among the developed materials, ZIF-8-AS, featuring both amine and thiol groups, demonstrates the fastest adsorption kinetics and a twofold increase in iodine adsorption capacity (qm = 1101.5 mg·g-1) compared to ZIF-8 (qm = 514.3 mg·g-1). Furthermore, the hierarchical mesoporosity of ZIF-8-A-10.1 improves CO2 adsorption to 1.0 mmol·g-1 at 298 K, which is 1.3 times higher than that of the microporous ZIF-8.