Investigation of Friction and Erosion Wear Properties of Titanium and Titanium Alloy Pipes

Titanium alloys are applied in oil and gas development and transportation to improve conditions because of their high specific strength and corrosion resistance. However, the disadvantage of poor wear resistance has become an obstacle to developing titanium alloys. The friction and wear properties of pure titanium TA3 and titanium alloy TA10 were tested under different loads and different friction forms using a reciprocating friction and wear tester. Moreover, the erosion resistance of pure titanium TA3 and titanium alloy TA10 was studied using a gas-solid erosion tester. The results show that the wear rate of TA3 and titanium alloy TA10 increases with increasing friction load. Under a load of 50 N, the mass losses of TA3 under dry friction and wet friction were 0.0013 g and 0.0045 g, respectively, while the mass losses of TA10 were 0.0033 g and 0.0046 g, respectively. While the load increased to 70 N, the mass loss of TA3 was even greater, reaching 0.0065 g, and the mass loss of TA10 was 0.0058 g. The wear forms of TA3 and TA10 include abrasive wear, adhesive wear and oxidation wear. The joint action of various friction forms leads to the loss of materials. Under the simulated working conditions, the erosion rates of TA3 and TA10 were 1.01 × 10^-3 g/s and 0.94 × 10^-3 g/s. The erosion mechanism is the same, including plowing, indentation and cracking.