The aim of the study: Was to elaborate and assess biocompatible compositions based on oligocarbonate methacrylate filled with hydroxyapatite.
Materials and methods: The manufacturing methods of the compositions are considered, and their polymerization ability, strength and elastic properties are evaluated.
Results: The highest values of hardness and elasticity were found in the composition containing 0.50% by weight of diphenyl (2.4,6-trimethylbenzoate)phosphine oxide and 10% by weight of hydroxyapatite. Its compressive strength was comparable to bone tissue and dental cements.
Conclusion: The described composition can be used as a model system for assessing the physical and mechanical properties of materials used to fill defects in dental tissue and bone.
Целью: Настоящей работы была разработка и изучение свойств биосовместимых композиций на основе олигокарбонатметакрилата, наполненных гидроксиапатитом.
Материалы и методы: Рассмотрены способы изготовления композиций, оценена их способность к полимеризации, прочностные и упругие свойства.
Результаты: Наиболее высокими значениями твердости и упругости характеризовалась композиция, содержащая 0,50% масс. дифенил (2,4,6-триметилбензоат)фосфиноксида и 10% масс. гидроксиапатита. Ее прочность на сжатие была сравнима с костной тканью и стоматологическими цементами.
Заключение: Описанная композиция может быть использована в качестве модельной системы для оценки физико-механических свойств материалов, используемых для восполнения дефектов тканей зубов и кости.
Keywords: 4; 6-trimethylbenzoyl) phosphine oxide; camphorquinone; composite materials; diphenyl (2; hydroxyapatite; oligocarbonate methacrylate; photopolymerizable composition.