Structural properties, dielectric relaxation and impedance spectroscopy of NASICON type Na$_{3+x}$Zr$_{2-x}$Pr$_{x}$Si$_2$PO$_{\rm 12}$ ceramics
Authors:
Ramcharan Meena,
Rajendra S. Dhaka
Abstract:
We investigate the dielectric and impedance spectroscopic investigation of Pr-doped NASICON type Na$_{3+x}$Zr$_{2-x}$Pr$_{x}$Si$_2$PO$_{\rm 12}$ ($x=$ 0.05--0.2) samples as a function of temperature and frequency. The Rietveld refinement of x-ray diffraction patterns confirms the monoclinic phase having C2/c space groups for all the samples. The scanning electron microscopy shows the granular-like…
▽ More
We investigate the dielectric and impedance spectroscopic investigation of Pr-doped NASICON type Na$_{3+x}$Zr$_{2-x}$Pr$_{x}$Si$_2$PO$_{\rm 12}$ ($x=$ 0.05--0.2) samples as a function of temperature and frequency. The Rietveld refinement of x-ray diffraction patterns confirms the monoclinic phase having C2/c space groups for all the samples. The scanning electron microscopy shows the granular-like structure and energy dispersive x-ray analysis confirms the desired compositions. The temperature (90--400~K) and frequency (20 Hz-2 MHz) dependence of electric permittivity are explained using Maxwell-Wagner-Sillars (MWS) polarization and space charge polarization mechanisms. The dielectric relaxation shows nearly equal activation energy for all the samples with a non-Debye type of relaxation in the measured temperature range. The complex impedance analysis shows the presence of broad grain and grain boundary relaxation peaks. The stretched exponent analysis of electric modulus using the Kohlrausch-Williams-Watts (KWW) function further confirms the non-Debye type of relaxation. Moreover, scaling analysis of the electric modulus shows a similar type of relaxation for all the samples. The {\it a.c.} conductivity data are fitted using modified power law, where the temperature dependence of exponent ($s$) confirms the correlated barrier hopping (CBH) type conduction for all the samples. Our results indicate that the Pr doped NASICON samples are potential candidates for charge storage devices due to their large electric permittivity.
△ Less
Submitted 19 May, 2024;
originally announced May 2024.
-
Temperature dependent conductivity, dielectric relaxation, electrical modulus and impedance spectroscopy of Ni substituted Na$_{3+2x}$Zr$_{2-x}$Ni$_{x}$Si$_2$PO$_{\rm 12}$
Authors:
Ramcharan Meena,
Rajendra S. Dhaka
Abstract:
We investigate the structural, dielectric relaxation, electric modulus and impedance behavior of Ni-doped NASICON ceramic Na$_{3+2x}$Zr$_{2-x}$Ni$_{x}$Si$_2$PO$_{\rm 12}$ ($x=$ 0.05--0.2) prepared using the solid-state reaction method. The increase in dielectric constant with temperature and decrease with frequency is explained on the basis of space charge polarization using the two-layer model of…
▽ More
We investigate the structural, dielectric relaxation, electric modulus and impedance behavior of Ni-doped NASICON ceramic Na$_{3+2x}$Zr$_{2-x}$Ni$_{x}$Si$_2$PO$_{\rm 12}$ ($x=$ 0.05--0.2) prepared using the solid-state reaction method. The increase in dielectric constant with temperature and decrease with frequency is explained on the basis of space charge polarization using the two-layer model of Maxwell-Wagner relaxation. The dielectric loss peak at lower temperatures follows the Arrhenius-type behavior with frequency having activation energy of 0.27$\pm$0.01~eV of dipolar relaxation, suggests similar type of defects are responsible for all the doped samples. The real ($ε$ $^{'}$) and imaginary ($ε$ $^{''}$) permittivity variation with frequency shows the broad relaxation behavior indicates the non-Debye type of relaxation in the measured temperature range. The permittivity values decrease with the amount of doping due to the increased number of charge carriers upon Ni doping at the Zr site. The grain contributions are observed at higher frequencies, while grain-boundary contributions occur at the lower side of frequencies. The imaginary part of the electric modulus also shows two types of relaxation peaks for all the samples indicating similar activation energy at low temperatures and variable activation energy at higher temperatures. The fitting of the imaginary modulus using KWW function shows the non-Debye type of relaxation. We find that all modulus curves merge with each other at low temperatures showing a similar type of relaxation, while curves at high temperatures show the dispersed behavior above the peak frequency. The {\it a.c.} conductivity data are fitted using the double power law confirming the grain and grain boundary contributions in total conductivity.
△ Less
Submitted 21 March, 2024;
originally announced March 2024.
-
Continuous Variable Based Quantum Communication in the Ocean
Authors:
Ramniwas Meena,
Subhashish Banerjee
Abstract:
Continuous Variable-Based Quantum Cryptography (CV-QKD) is an emerging field in quantum information science, offering unprecedented security for communication protocols by harnessing the principles of quantum mechanics. However, ocean environments pose unique challenges to quantum communication due to their distinct properties and characteristics. This work investigates the impact of turbulence on…
▽ More
Continuous Variable-Based Quantum Cryptography (CV-QKD) is an emerging field in quantum information science, offering unprecedented security for communication protocols by harnessing the principles of quantum mechanics. However, ocean environments pose unique challenges to quantum communication due to their distinct properties and characteristics. This work investigates the impact of turbulence on the transmission of Gaussian light beams used in a continuous variable-based quantum key distribution system for underwater quantum communication. The objective is to quantitatively analyze the induced losses and propose methodologies to mitigate their effects. To achieve this, we adopt the widely accepted ABCD matrix formalism, which provides a comprehensive framework for characterizing the propagation of optical beams through different media. Moreover, a numerical simulation framework is developed to assess the resulting losses and evaluate the performance of the proposed system. The implications of these numerical simulation frameworks for the design and optimization of quantum communication systems for oceanic environments are thoroughly discussed.
△ Less
Submitted 24 January, 2024;
originally announced January 2024.
-
Analysing QBER and secure key rate under various losses for satellite based free space QKD
Authors:
Muskan,
Ramniwas Meena,
Subhashish Banerjee
Abstract:
Quantum Key Distribution is a key distribution method that uses the qubits to safely distribute one-time use encryption keys between two or more authorised participants in a way that ensures the identification of any eavesdropper. In this paper, we have done a comparison between the BB84 and B92 protocols and BBM92 and E91 entanglement based protocols for satellite based uplink and downlink in low…
▽ More
Quantum Key Distribution is a key distribution method that uses the qubits to safely distribute one-time use encryption keys between two or more authorised participants in a way that ensures the identification of any eavesdropper. In this paper, we have done a comparison between the BB84 and B92 protocols and BBM92 and E91 entanglement based protocols for satellite based uplink and downlink in low Earth orbit. The expressions for the quantum bit error rate and the keyrate are given for all four protocols. The results indicate that, when compared to the B92 protocol, the BB84 protocol guarantees the distribution of a higher secure keyrate for a specific distance. Similarly, it is observed that BBM92 ensures higher keyrate in comparison with E91 protocol.
△ Less
Submitted 12 January, 2024; v1 submitted 2 August, 2023;
originally announced August 2023.
-
Effect of the growth orientation on the physical properties of Sr$_2$CoNbO$_6$ thin films
Authors:
Ajay Kumar,
Ramcharan Meena,
M. Miryala,
K. Ueno,
Rajendra S. Dhaka
Abstract:
We study the effect of the growth orientation on the structural, electronic, and hence transport properties of Sr$_2$CoNbO$_6$ thin films grown on the orthorhombic NGO(100) and cubic MgO(100) substrates. The x-ray diffraction patterns show the growth of the thin film along $a$-axis resulting in the asymmetric ($b\neq c$) in-plane compressive strain in case of NGO(100), whereas along $c$-axis with…
▽ More
We study the effect of the growth orientation on the structural, electronic, and hence transport properties of Sr$_2$CoNbO$_6$ thin films grown on the orthorhombic NGO(100) and cubic MgO(100) substrates. The x-ray diffraction patterns show the growth of the thin film along $a$-axis resulting in the asymmetric ($b\neq c$) in-plane compressive strain in case of NGO(100), whereas along $c$-axis with tensile strain in case of MgO(100) substrate. The temperature dependent resistivity measurements indicate the lower electronic conductivity for the film grown on the NGO(100) substrate, which is found to be correlated with the higher degree of the oxygen deficiencies and hence larger concentration of the insulating Co$^{2+}$ in this sample. Further, the x-ray photoemission spectroscopy measurements show that Sr and Nb are present in the 2+ and 4+ valence state, whereas Co exist in the 2+, 3+ as well as 4+ states, fraction of which was found to vary with the growth orientation. Moreover, the analysis of leakage current using the sum exponent model indicate the presence of two different relaxation mechanisms in these samples.
△ Less
Submitted 11 June, 2023;
originally announced June 2023.
-
Characterization of Quantumness of non-Gaussian states under the influence of Gaussian channel
Authors:
Ramniwas Meena,
Subhashish Banerjee
Abstract:
The impact of a noisy Gaussian channel on a wide range of non-Gaussian input states is studied in this work. The nonclassical nature of the states, both input and output, is developed by studying the corresponding photon statistics and quasi-probability distributions. It is found that photon addition has more robust quantum mechanical properties as compared to the photon subtraction case. The thre…
▽ More
The impact of a noisy Gaussian channel on a wide range of non-Gaussian input states is studied in this work. The nonclassical nature of the states, both input and output, is developed by studying the corresponding photon statistics and quasi-probability distributions. It is found that photon addition has more robust quantum mechanical properties as compared to the photon subtraction case. The threshold value of the noise parameter corresponding to the transition from partial negative (W and P ) and zero (Q) to completely positive definite, at the center of phase space, depends not only on the average number of thermal photons in the state, but also on the squeezing parameter. In addition it is observed that the nonclassicality of the kth-number filtrated thermal state could be further enhanced by adding photon(s).
△ Less
Submitted 22 December, 2022;
originally announced December 2022.
-
Quantifying the Structure of Disordered Materials
Authors:
Thomas J. Hardin,
Michael Chandross,
Rahul Meena,
Spencer Fajardo,
Dimitris Giovanis,
Ioannis G. Kevrekidis,
Michael Falk,
Michael Shields
Abstract:
Durable interest in developing a framework for the detailed structure of glassy materials has produced numerous structural descriptors that trade off between general applicability and interpretability. However, none approach the combination of simplicity and wide-ranging predictive power of the lattice-grain-defect framework for crystalline materials. Working from the hypothesis that the local ato…
▽ More
Durable interest in developing a framework for the detailed structure of glassy materials has produced numerous structural descriptors that trade off between general applicability and interpretability. However, none approach the combination of simplicity and wide-ranging predictive power of the lattice-grain-defect framework for crystalline materials. Working from the hypothesis that the local atomic environments of a glassy material are constrained by enthalpy minimization to a low-dimensional manifold in atomic coordinate space, we develop a novel generalized distance function, the Gaussian Integral Inner Product (GIIP) distance, in connection with agglomerative clustering and diffusion maps, to parameterize that manifold. Applying this approach to a two-dimensional model crystal and a three-dimensional binary model metallic glass results in parameters interpretable as coordination number, composition, volumetric strain, and local symmetry. In particular, we show that a more slowly quenched glass has a higher degree of local tetrahedral symmetry at the expense of cyclic symmetry. While these descriptors require post-hoc interpretation, they minimize bias rooted in crystalline materials science and illuminate a range of structural trends that might otherwise be missed.
△ Less
Submitted 14 November, 2022;
originally announced November 2022.
-
Dielectric properties and impedance spectroscopy of NASICON type Na$_3$Zr$_2$Si$_2$PO$_{12}$
Authors:
Ramcharan Meena,
Rajendra S. Dhaka
Abstract:
We report the temperature dependent dielectric properties and impedance spectroscopy investigation of Na$_3$Zr$_2$Si$_2$PO$_{12}$ in the frequency range of 20 Hz--2 MHz. The Rietveld refinement of x-ray diffraction pattern confirms the monoclinic phase with C2/c space group. The {\it d.c.} resistivity behavior shows its strong insulating nature at low temperatures, and follows Arrhenius law of the…
▽ More
We report the temperature dependent dielectric properties and impedance spectroscopy investigation of Na$_3$Zr$_2$Si$_2$PO$_{12}$ in the frequency range of 20 Hz--2 MHz. The Rietveld refinement of x-ray diffraction pattern confirms the monoclinic phase with C2/c space group. The {\it d.c.} resistivity behavior shows its strong insulating nature at low temperatures, and follows Arrhenius law of thermal conduction with an activation energy of 0.68 eV. The decrease in electric permittivity ($ε_r$) with frequency is explained based on the space polarization mechanism and its increment with temperature by thermal activation of charge carriers. The dielectric loss (D=tan$δ$) peak follows the Arrhenius law of thermal activation with an energy of 0.25 eV. We observe an enhancement in {\it a.c.} conductivity with frequency and temperature due to the decrease in the activation energy, which results in enhancing the conduction between defect states. Further, we observe an abrupt increase in the {\it a.c.} conductivity at high frequencies, which is explained using the universal Jonschers power law. The analysis of {\it a.c.} conductivity shows two types of conduction mechanisms namely correlated barrier hopping and non-overlapping small polaron tunnelling in the measured temperature range. The imaginary part of the electric modulus confirms the non-Debye type relaxation in the sample. The shifting of the relaxation peak towards higher frequency side with an increase in temperature ensures its thermally activated nature. The scaling behavior of the electric modulus shows similar type of relaxation over the measured temperature range. The combined analysis of electric modulus and impedance with frequency shows the short-range mobility of charge carriers.
△ Less
Submitted 7 June, 2022;
originally announced June 2022.
-
Ground-state properties of the narrowest zigzag graphene nanoribbon from quantum Monte Carlo and comparison with density functional theory
Authors:
Raghavendra Meena,
Guanna Li,
Michele Casula
Abstract:
By means of quantum Monte Carlo (QMC) calculations from first principles, we study the ground-state properties of the narrowest zigzag graphene nanoribbon, with an infinite linear acene structure. We show that this quasi-one-dimensional system is correlated and its ground state is made of localized $π$ electrons whose spins are antiferromagnetically (AFM) ordered. The AFM stablization energy (36(3…
▽ More
By means of quantum Monte Carlo (QMC) calculations from first principles, we study the ground-state properties of the narrowest zigzag graphene nanoribbon, with an infinite linear acene structure. We show that this quasi-one-dimensional system is correlated and its ground state is made of localized $π$ electrons whose spins are antiferromagnetically (AFM) ordered. The AFM stablization energy (36(3) meV per carbon atom) and the absolute magnetization (1.13(1) $μ_\textrm{B}$ per unit cell) predicted by QMC are sizable, and they suggest the survival of antiferromagnetic correlations above room temperature. These values can be reproduced to some extent by density functional theory (DFT) only by assuming strong interactions, either within the DFT+U framework or using hybrid functionals. Based on our QMC results, we then provide the strength of Hubbard repulsion in DFT+U suitable for this class of systems.
△ Less
Submitted 11 November, 2021;
originally announced November 2021.
-
Raman Spectroscopy of Bi2Se3-xTex (x= 0 to 3) Topological Insulator Crystals
Authors:
Deepak Sharma,
M. M. Sharma,
R. S. Meena,
V. P. S. Awana
Abstract:
We report crystal growth and Raman spectroscopy characterization of pure and mixed bulk topological insulators. The series comprises of both binary and ternary tetradymite topological insulators. We analyzed in detail the Raman peaks of vibrational modes as out of plane Ag, and in plane Eg for both binary and ternary tetradymite topological insulators. Both out of plane Ag exhibit obvious atomic s…
▽ More
We report crystal growth and Raman spectroscopy characterization of pure and mixed bulk topological insulators. The series comprises of both binary and ternary tetradymite topological insulators. We analyzed in detail the Raman peaks of vibrational modes as out of plane Ag, and in plane Eg for both binary and ternary tetradymite topological insulators. Both out of plane Ag exhibit obvious atomic size dependent peak shifts and the effect is much lesser for the former than the latter. The situation is rather interesting for in plane Eg, which not only shows the shift but rather a broader hump like structure. The de convolution of the same show two clear peaks, which are understood in terms of the presence of separate in plane BiSe and BiTe modes in mixed tetradymite topological insulators. Summarily, various Raman modes of well-characterized pure and mixed topological insulator single crystals are reported and discussed in this article.
△ Less
Submitted 26 August, 2020;
originally announced August 2020.
-
Estimation after selection from bivariate normal population using LINEX loss function
Authors:
Mohd. Arshad,
Omer Abdalghani,
Kalu Ram Meena
Abstract:
Let $π_1$ and $π_2$ be two independent populations, where the population $π_i$ follows a bivariate normal distribution with unknown mean vector $\boldsymbolθ^{(i)}$ and common known variance-covariance matrix $Σ$, $i=1,2$. The present paper is focused on estimating a characteristic $θ_{\textnormal{y}}^S$ of the selected bivariate normal population, using a LINEX loss function. A natural selection…
▽ More
Let $π_1$ and $π_2$ be two independent populations, where the population $π_i$ follows a bivariate normal distribution with unknown mean vector $\boldsymbolθ^{(i)}$ and common known variance-covariance matrix $Σ$, $i=1,2$. The present paper is focused on estimating a characteristic $θ_{\textnormal{y}}^S$ of the selected bivariate normal population, using a LINEX loss function. A natural selection rule is used for achieving the aim of selecting the best bivariate normal population. Some natural-type estimators and Bayes estimator (using a conjugate prior) of $θ_{\textnormal{y}}^S$ are presented. An admissible subclass of equivariant estimators, using the LINEX loss function, is obtained. Further, a sufficient condition for improving the competing estimators of $θ_{\textnormal{y}}^S$ is derived. Using this sufficient condition, several estimators improving upon the proposed natural estimators are obtained. Further, a real data example is provided for illustration purpose. Finally, a comparative study on the competing estimators of $θ_{\text{y}}^S$ is carried-out using simulation.
△ Less
Submitted 13 November, 2019;
originally announced November 2019.
-
Hikami-Larkin-Nagaoka (HLN) Fitting of Magneto Transport of Bi2Se3 Single Crystal in Different Magnetic Field Ranges
Authors:
Deepak Sharma,
P. Rani,
P. K. Maheshwari,
V. Nagpal,
R. S. Meena,
S. S. Islam,
S. Patnaik,
V. P. S. Awana
Abstract:
We report the detailed study of structural micro-structuraland high magnetic field magneto transport propertiesof Bi2Se3single crystal. Bi2Se3 single crystal is grown through conventional solid-state reaction route via the self-flux method. Rietveld analysis on Powder X-ray Diffraction showed that the studied Bi2Se3 crystal is crystallized in single-phase without any impurity. The surface morpholo…
▽ More
We report the detailed study of structural micro-structuraland high magnetic field magneto transport propertiesof Bi2Se3single crystal. Bi2Se3 single crystal is grown through conventional solid-state reaction route via the self-flux method. Rietveld analysis on Powder X-ray Diffraction showed that the studied Bi2Se3 crystal is crystallized in single-phase without any impurity. The surface morphology analyzed through Scanning Electron Microscopy study which shows that as-grown single crystal exhibit layered type structure and the quantitative weight of the atomic constituents (Bi and Se) are found to be closeto the stoichiometric amount in energy-dispersive X-ray spectroscopy analysis. Low temperature (2.5K) magneto-resistance (MR) exhibited a v-type cusp around origin at lower magnetic field, which is the sign of weak anti-localization effect. Further, Bi2Se3 single crystal magneto conductivity data is fitted by well-known HLN equation in different magnetic field range of 2Tesla, 4Tesla and 6Tesla and the resultant found that the conduction mechanism of Bi2Se3 is dominated by WAL state.
△ Less
Submitted 28 October, 2019;
originally announced October 2019.
-
Role of oxygen interstitials in Zn1-xGaxO for faster response to UV light
Authors:
Prashant Kumar Mishra,
Tulika Srivastava,
Saniya Ayaz,
Ramraj Meena,
Sajal Biring,
Somaditya Sen
Abstract:
ZnO doped with Gallium (Ga3+) demonstrates better crystalline nature and conductivity increases. Latent defect states are suppressed. However, due to the larger charge of Ga3+ oxygen interstitials are generated which control the sensing speed. The conductance increases as a consequence of reduced defect states, especially the oxygen vacancies. The photocurrent increases with Galium incorporation,…
▽ More
ZnO doped with Gallium (Ga3+) demonstrates better crystalline nature and conductivity increases. Latent defect states are suppressed. However, due to the larger charge of Ga3+ oxygen interstitials are generated which control the sensing speed. The conductance increases as a consequence of reduced defect states, especially the oxygen vacancies. The photocurrent increases with Galium incorporation, but a more intense increase in the current reduces the sensitivity.
△ Less
Submitted 24 February, 2019;
originally announced February 2019.
-
Novel solid state vacuum quartz encapsulated growth of p-Terphenyl: the parent High Tc Oraganic Superconductor (HTOS)
Authors:
P. K. Maheshwari,
R. S. Meena,
Bhasker Gahtori,
Reena Goyal,
Rabia Sultana,
Poonam Rani,
V. P. S. Awana
Abstract:
We report an easy and versatile route for the synthesis of the parent phase of newest superconducting wonder material i.e. p-Terphenyl. Doped p-terphenyl has recently shown superconductivity with transition temperature as high as 120K. For crystal growth, the commercially available p-Terphenyl powder is pelletized, encapsulated in evacuated (10-4 Torr) quartz tube and subjected to high temperature…
▽ More
We report an easy and versatile route for the synthesis of the parent phase of newest superconducting wonder material i.e. p-Terphenyl. Doped p-terphenyl has recently shown superconductivity with transition temperature as high as 120K. For crystal growth, the commercially available p-Terphenyl powder is pelletized, encapsulated in evacuated (10-4 Torr) quartz tube and subjected to high temperature (260C) melt followed by slow cooling at 5C/hour. Simple temperature controlled heating furnace is used during the process. The obtained crystal is one piece, shiny and plate like. Single crystal surface XRD (X-ray Diffraction) showed unidirectional (00l) lines, indicating that the crystal is grown along c-direction. Powder XRD of the specimen showed that as grown p-Terphenyl is crystallized in monoclinic structure with space group P21/a space group, having lattice parameters a = 8.08(2) A, b = 5.62(5) A and c= 13.58(3) A. Scanning electron microscopy (SEM) pictures of the crystal showed clear layered slab like growth without any visible contamination from oxygen. Characteristic reported Raman active modes related to C-C-C bending, C-H bending, C-C stretching and C-H stretching vibrations are seen clearly for the studied p-Terphenyl crystal. The physical properties of crystal are yet underway. The short letter reports an easy and versatile crystal growth method for obtaining quality p-terphenyl. The same growth method may probably be applied to doped p-terphenyl and to subsequently achieve superconductivity to the tune of as high 120K for the newest superconductivity wonder i.e., High Tc Oraganic Superconductor (HTOS).
△ Less
Submitted 8 June, 2017; v1 submitted 6 June, 2017;
originally announced June 2017.
-
Structural, Magnetic and Magneto-caloric studies of Ni50Mn30Sn20Shape Memory Alloy
Authors:
Ramesh Chandra Bhatt,
R. S. Meena,
H. Kishan,
V. P. S. Awana,
S. K. Agarwal
Abstract:
We have synthesized a nominal composition of Ni50Mn30Sn20 alloy using arc melting technique. Rietveld refinement confirms the austenite L21 structure in Fm-3m space group. Electrical resistivity has been found to clearly exhibiting two different phenomena viz. a magnetic transition from paramagnetic to ferromagnetic and a structural transition from austenite to martensitic phase. Thermo-magnetizat…
▽ More
We have synthesized a nominal composition of Ni50Mn30Sn20 alloy using arc melting technique. Rietveld refinement confirms the austenite L21 structure in Fm-3m space group. Electrical resistivity has been found to clearly exhibiting two different phenomena viz. a magnetic transition from paramagnetic to ferromagnetic and a structural transition from austenite to martensitic phase. Thermo-magnetization measurements M(T) confirms ferromagnetic transition temperature TC at 222 K and martensitic transition starting at 127 K(MS). Magnetization measurement M(H) at 10 K confirms the ferromagnetic state. Frequency dependence of ac susceptibility \c{hi}' at low temperature suggests spin glass behavior in the system. The isothermal magnetic entropy change values have been found to be 1.14 J/Kg.K, 2.69 J/Kg.K and 3.9 J/Kg.K, with refrigeration capacities of 19.6 J/kg, 37.8 J/kg and 54.6 J/kg for the field change of 1, 2 and 3 Tesla respectively at 227 K.
△ Less
Submitted 5 November, 2015;
originally announced November 2015.
-
A novel ZnO piezoelectric microcantilever energy scavenger: Fabrication and characterization
Authors:
Deepak Bhatia,
Himanshu Sharma,
R. S. Meena,
V. R Palkar
Abstract:
This novel piezoelectric zinc oxide (ZnO) thin film microcantilever was fabricated by micromachining technique. To release the cantilever, wet anisotropic etching of Silicon (Si) was performed by tetramethyl ammonium hydroxide (TMAH). The transverse piezoelectric coefficient d31 of the ZnO film, obtained from the deflection of the cantilever with influence of applied voltage, was calculated as 3.3…
▽ More
This novel piezoelectric zinc oxide (ZnO) thin film microcantilever was fabricated by micromachining technique. To release the cantilever, wet anisotropic etching of Silicon (Si) was performed by tetramethyl ammonium hydroxide (TMAH). The transverse piezoelectric coefficient d31 of the ZnO film, obtained from the deflection of the cantilever with influence of applied voltage, was calculated as 3.32 pC/N. The observed dynamic characterization of the novel piezoelectric microcantilever had linear response with the applied driving voltage. The obtained values of Young Modulus and Hardness were 208 +4 GPa and 4.84+ 0.1 GPa respectively. This inexpensive novel method provides additional design flexibility to fabricate vibrational energy harvesters. The easy steps of fabrication and cost effectiveness of this method may be preferred it over DRIE. The voltage induced due to deformation of ZnO cantilever were measured ~230mV. This microcantilever energy scavenger may be used to power the nano devices and sensors for medical and agricultural applications as a replacement of traditional bulky batteries.
△ Less
Submitted 5 June, 2016; v1 submitted 19 June, 2015;
originally announced June 2015.
-
Investigation of Magnetic Domain Structure in Bi0.7Dy0.3FeO3 thin films integrated with ZnO film
Authors:
Deepak Bhatia,
Himanshu Sharma,
Seeraj Nawaj,
R. S. Meena,
C. V. Tomy,
V. R Palkar
Abstract:
The magnetic domain structure of the multiferroic Bi1-xDyxFeO3 (BDFO) deposited on ZnO at the macroscopic level has been demonstrated in this paper. Magnetic properties are observed by saturated magnetic and ferroelectric hysteresis loops at room temperature. The coupling behaviour and magnetic transition are verified using Multimode Atomic Force Microscope by applying bias between sample and MFM…
▽ More
The magnetic domain structure of the multiferroic Bi1-xDyxFeO3 (BDFO) deposited on ZnO at the macroscopic level has been demonstrated in this paper. Magnetic properties are observed by saturated magnetic and ferroelectric hysteresis loops at room temperature. The coupling behaviour and magnetic transition are verified using Multimode Atomic Force Microscope by applying bias between sample and MFM tip. ZnO thin film of 300 nm was deposited by dielectric sputtering using a ZnO target on Si p-type conducting (.0001-0005 Ω cm) substrate. BDFO thin films of 300 nm were deposited on Si/ZnO using PLD (Pulsed laser deposition) technique. It is observed that BDFO thin films integrated with ZnO film shows the coexistence of ferromagnetic and ferroelectric ordering with significant coupling at room temperature. Integration of BDFO films with ZnO piezoelectric thin film shows the potential in MEMS applications as well as in Memory devices and strong history dependent systems.
△ Less
Submitted 11 March, 2015;
originally announced March 2015.
-
Structural and Dielectric Characterization on Multiferroic xNi0.9Zn0.1Fe2O4/(1-x)PbZr0.52Ti0.48O3 Particulate Composite
Authors:
Rishikesh Pandey,
Braj Raj Meena,
Akhilesh Kumar Singh
Abstract:
We have carried out the powder x-ray diffraction and dielectric studies on multiferroic particulate composite xNi0.9Zn0.1Fe2O4/(1-x)PbZr0.52Ti0.48O3 with x=0.15, 0.30, 0.45, 0.60, 0.75 and 0.90 to explore the structural and ferroelectric properties. A conventional double sintering method was used to prepare the xNi0.9Zn0.1Fe2O4/(1-x)PbZr0.52Ti0.48O3 composites. The structure of one of the componen…
▽ More
We have carried out the powder x-ray diffraction and dielectric studies on multiferroic particulate composite xNi0.9Zn0.1Fe2O4/(1-x)PbZr0.52Ti0.48O3 with x=0.15, 0.30, 0.45, 0.60, 0.75 and 0.90 to explore the structural and ferroelectric properties. A conventional double sintering method was used to prepare the xNi0.9Zn0.1Fe2O4/(1-x)PbZr0.52Ti0.48O3 composites. The structure of one of the component Ni0.9Zn0.1Fe2O4 is spinel cubic with space group Fd3m, while the other component PbZr0.52Ti0.48O3 is selected around the morphotropic phase boundary region in which the tetragonal and monoclinic phases with space group P4mm and Cm coexist respectively. We have carried out Rietveld refinement of the structure to check the formation of ideal composites with separate ferroelectric and ferrite phases. Even though the structural characterization does not reveal the formation of any new phase due to reaction between the two components of the composite during sintering, the tetragonality of the PbZr0.52Ti0.48O3 continuously decreases with increasing the ferrite fraction while the lattice parameter of ferrite phase increases with increasing fraction of the ferroelectric phase. Similarly, the dielectric study reveals clear shift in the ferroelectric to paraelectric phase transition temperature of PbZr0.52Ti0.48O3 during composite formation suggesting that part of Ni2+, Zn2+/ Fe3+ ions are diffusing at the B-site of PbZr0.52Ti0.48O3 replacing Ti4+, which in turn decreases its transition temperature. Scanning electron micrograph of sintered pellet surface confirms the presence of two types of particle morphology in the particulate composite, corresponding to ferrite and ferroelectric phases.
△ Less
Submitted 19 February, 2014; v1 submitted 25 November, 2013;
originally announced November 2013.
-
Anomaly Detections in Internet traffic Using Empirical Measures
Authors:
A. S. Syed Navaz,
S. Gopalakrishnan,
R. Meena
Abstract:
Introducing Internet traffic anomaly detection mechanism based on large deviations results for empirical measures. Using past traffic traces we characterize network traffic during various time-of-day intervals, assuming that it is anomaly-free. Throughout, we compare the two approaches presenting their advantages and disadvantages to identify and classify temporal network anomalies. We also demons…
▽ More
Introducing Internet traffic anomaly detection mechanism based on large deviations results for empirical measures. Using past traffic traces we characterize network traffic during various time-of-day intervals, assuming that it is anomaly-free. Throughout, we compare the two approaches presenting their advantages and disadvantages to identify and classify temporal network anomalies. We also demonstrate how our framework can be used to monitor traffic from multiple network elements in order to identify both spatial and temporal anomalies. We validate our techniques by analyzing real traffic traces with time-stamped anomalies.
△ Less
Submitted 24 August, 2013;
originally announced August 2013.
-
Electrical and Magnetic behaviour of PrFeAsO0.8F0.2 superconductor
Authors:
R S Meena,
Anand Pal,
K V R Rao,
Hari Kishan,
V. P. S. Awana
Abstract:
The superconducting and ground state samples of PrFeAsO0.8F0.2 and PrFeAsO have been synthesised via easy and versatile single step solid state reaction route. X-ray & Reitveld refine parameters of the synthesised samples are in good agreement to the earlier reported value of the structure. The ground state of the pristine compound (PrFeAsO) exhibited a metallic like step in resistivity below 150K…
▽ More
The superconducting and ground state samples of PrFeAsO0.8F0.2 and PrFeAsO have been synthesised via easy and versatile single step solid state reaction route. X-ray & Reitveld refine parameters of the synthesised samples are in good agreement to the earlier reported value of the structure. The ground state of the pristine compound (PrFeAsO) exhibited a metallic like step in resistivity below 150K followed by another step at 12K. The former is associated with the spin density wave (SDW) like ordering of Fe spins and later to the anomalous magnetic ordering for Pr moments. Both the resistivity anomalies are absent in case of superconducting PrFeAsO0.8F0.2 sample. Detailed high field (up to 12Tesla) electrical and magnetization measurements are carried out for superconducting PrFeAsO0.8F0.2 sample. The PrFeAsO0.8F0.2 exhibited superconducting onset (Tconset) at around 47K with Tc(ρ =0) at 38K. Though the Tconset remains nearly invariant, the Tc(ρ =0) is decreased with applied field, and the same is around 23K under applied field of 12Tesla. The upper critical field (Hc2) is estimated from the Ginzburg Landau equation (GL) fitting, which is found to be ~ 182Tesla. Critical current density (Jc) being calculated from high field isothermal magnetization (MH) loops with the help of Beans critical state model, is found to be of the order of 103 A/cm2. Summarily, the superconductivity characterization of single step synthesised PrFeAsO0.8F0.2 superconductor is presented.
△ Less
Submitted 7 February, 2014; v1 submitted 16 August, 2013;
originally announced August 2013.
-
Magneto-transport and magnetic susceptibility of SmFeAsO1-xFx (x = 0.0 and 0.20)
Authors:
R. S. Meena,
Anand Pal,
Shiva Kumar,
K. V. R Rao,
V. P. S. Awana
Abstract:
Bulk polycrystalline samples, SmFeAsO and the iso-structural superconducting SmFeAsO0.80F0.20 are explored through resistivity with temperature under magnetic field ρ(T, H), AC and DC magnetization (M-T), and Specific heat (Cp) measurements. The Resistivity measurement shows superconductivity for x = 0.20 sample with Tc(onset) ~ 51.7K. The upper critical field, [Hc2(0)] is estimated ~3770kOe by Gi…
▽ More
Bulk polycrystalline samples, SmFeAsO and the iso-structural superconducting SmFeAsO0.80F0.20 are explored through resistivity with temperature under magnetic field ρ(T, H), AC and DC magnetization (M-T), and Specific heat (Cp) measurements. The Resistivity measurement shows superconductivity for x = 0.20 sample with Tc(onset) ~ 51.7K. The upper critical field, [Hc2(0)] is estimated ~3770kOe by Ginzburg-Landau (GL) theory. Broadening of superconducting transition in magneto transport is studied through thermally activated flux flow in applied field up to 130 kOe. The flux flow activation energy (U/kB) is estimated ~1215K for 1kOe field. Magnetic measurements exhibited bulk superconductivity with lower critical field (Hc1) of ~1.2kOe at 2K. In normal state, the paramagnetic nature of compound confirms no trace of magnetic impurity which orders ferromagnetically. AC susceptibility measurements have been carried out for SmFeAsO0.80F0.20 sample at various amplitude and frequencies of applied AC drive field. The inter-granular critical current density (Jc) is estimated. Specific heat [Cp(T)] measurement showed an anomaly at around 140K due to the SDW ordering of Fe, followed by another peak at 5K corresponding to the antiferromagnetic (AFM) ordering of Sm+3 ions in SmFeAsO compound. Interestingly the change in entropy (marked by the Cp transition height) at 5K for Sm+3 AFM ordering is heavily reduced in case of superconducting SmFeAsO0.80F0.20 sample.
△ Less
Submitted 17 July, 2013; v1 submitted 3 September, 2012;
originally announced September 2012.
-
Spin-fluctuations in Ti$_{60}$V$_{40}$ alloy and its influence on the superconductivity
Authors:
Md Matin,
L S Sharath Chandra,
Radhakishan Meena,
M K Chattopadhyay,
S B Roy
Abstract:
We report experimental studies of the temperature and magnetic field dependence of resistivity and dc magnetic susceptibility and the temperature dependence of zero field heat capacity in a Ti$_{0.6}$V$_{0.4}$ alloy. The temperature dependence of the normal state dc magnetic susceptibility in this Ti$_{0.6}$V$_{0.4}$ alloy shows T$^2$lnT behavior. The temperature dependence of resistivity follows…
▽ More
We report experimental studies of the temperature and magnetic field dependence of resistivity and dc magnetic susceptibility and the temperature dependence of zero field heat capacity in a Ti$_{0.6}$V$_{0.4}$ alloy. The temperature dependence of the normal state dc magnetic susceptibility in this Ti$_{0.6}$V$_{0.4}$ alloy shows T$^2$lnT behavior. The temperature dependence of resistivity follows a T$^2$ behaviour in the range 20-50 K. On the other hand, a term $T^3$ lnT is needed in the expression containing the electronic and lattice heat capacities to explain the temperature dependence of heat capacity at temperatures where $T^2$ dependence of resistivity is observed. Such temperature dependence of dc magnetic susceptibility, resistivity and heat capacity are indications of the presence of spin-fluctuations in the system. Further experimental evidence for the spin fluctuations is obtained in the form of a negative value of T$^5$ term in the temperature dependence of resistivity. The influence of spin-fluctuations on the superconducting properties of Ti$_{0.6}$V$_{0.4}$ is discussed in detail. We show from our analysis of resistivity and the susceptibility in normal and superconducting states that the spin fluctuations present in Ti$_{0.6}$V$_{0.4}$ alloy are itinerant in nature. There is some evidence of the existence of preformed Cooper-pairs in the temperature range well above the superconducting transition temperature. Our study indicates that the interesting correlations between spin-fluctuations and superconductivity may actually be quite widespread amongst the superconducting materials, and not necessarily be confined only to certain classes of exotic compounds.
△ Less
Submitted 27 August, 2013; v1 submitted 1 August, 2012;
originally announced August 2012.
-
High Field (14Tesla) Magneto Transport of Sm/PrFeAsO
Authors:
R. S. Meena,
Shiva Kumar Singh,
Anand Pal,
Anuj Kumar,
R. Jha,
K. V. R. Rao,
Yi. Du,
X. L. Wang,
V. P. S Awana
Abstract:
We report high field magneto transport of Sm/PrFeAsO. Below spin density wave transition (TSDW), the magneto-resistance (MR) of Sm/PrFeAsO is positive and increasing with decreasing temperature. The MR of SmFeAsO, is found 16%, whereas the same is 21.5% in case of PrFeAsO, at 2.5 K under applied magnetic field of 14 Tesla (T). In case of SmFeAsO, the variation of isothermal MR with field below 20…
▽ More
We report high field magneto transport of Sm/PrFeAsO. Below spin density wave transition (TSDW), the magneto-resistance (MR) of Sm/PrFeAsO is positive and increasing with decreasing temperature. The MR of SmFeAsO, is found 16%, whereas the same is 21.5% in case of PrFeAsO, at 2.5 K under applied magnetic field of 14 Tesla (T). In case of SmFeAsO, the variation of isothermal MR with field below 20 K is nonlinear at lower magnetic fields (< 2 Tesla) and the same is linear at moderately higher magnetic fields (H \geq 3.5 T). On the other hand PrFeAsO shows almost linear MR at all temperatures below 20 K. The anomalous behavior of MR being exhibited in PrFeAsO is originated from Dirac cone states. The stronger interplay of Fe and Pr ordered moments is responsible for this distinct behavior. PrFeAsO also shows a hump in resistivity (R-T) with possible conduction band (FeAs) mediated ordering of Pr moments at around 12 K. However the same is absent in SmFeAsO even down to 2 K. Our results of high field magneto-transport of up to 14 Tesla brings about clear distinction between ground states of SmFeAsO and PrFeAsO.
△ Less
Submitted 15 March, 2012; v1 submitted 14 November, 2011;
originally announced November 2011.
-
Physical property characterization of single step synthesized NdFeAsO0.80F0.20 bulk 50K superconductor
Authors:
V. P. S. Awana,
R. S. Meena,
Anand Pal,
Arpita Vajpayee,
K. V. R. Rao,
H. Kishan
Abstract:
We report an easy single step synthesis route of title compound NdFeAsO0.80F0.20 superconductor having bulk superconductivity below 50 K. The title compound is synthesized via solid-state reaction route by encapsulation in an evacuated (10-3 Torr) quartz tube. Rietveld analysis of powder X-ray diffraction data shows that compound crystallized in tetragonal structure with space group P4/nmm. R(T)H…
▽ More
We report an easy single step synthesis route of title compound NdFeAsO0.80F0.20 superconductor having bulk superconductivity below 50 K. The title compound is synthesized via solid-state reaction route by encapsulation in an evacuated (10-3 Torr) quartz tube. Rietveld analysis of powder X-ray diffraction data shows that compound crystallized in tetragonal structure with space group P4/nmm. R(T)H measurements showed superconductivity with Tc (R=0) at 48 K and a very high upper critical field (Hc2) of up to 345 Tesla. Magnetic measurements exhibited bulk superconductivity in terms of diamagnetic onset below 50 K. The lower critical field (Hc1) is around 1000 Oe at 5 K. In normal state i.e., above 60 K, the compound exhibited purely paramagnetic behavior and thus ruling out the presence of any ordered FeOx impurity in the matrix. In specific heat measurements a jump is observed in the vicinity of superconducting transition (Tc) along with an upturn at below T=4 K due to the AFM ordering of Nd+3 ions in the system. The Thermo-electric power (TEP) is negative down to Tc, thus indicating dominant carriers to be of n-type in NdFeAsO0.80F0.20 superconductor. The granularity of the bulk superconducting NdFeAsO0.8F0.2 sample is investigated and the intra and inter grain contributions have been individuated by looking at various amplitude and frequencies of the applied AC drive magnetic field.
△ Less
Submitted 20 January, 2012; v1 submitted 1 March, 2010;
originally announced March 2010.
-
Single step synthesis of Sr4V2O6Fe2As2: The blocking layer based potential future superconductor
Authors:
Anand Pal,
Arpita Vajpayee,
R. S. Meena,
H. Kishan,
V. P. S. Awana
Abstract:
We report synthesis, structural details and transport measurements on Sr4V2O6Fe2As2. Namely the stoichiometric amounts of V2O5 + SrO2 + Sr + 2FeAs are weighed mixed, ground thoroughly and palletized in rectangular form in a glove box in high purity Ar atmosphere. The pellet is further sealed in an evacuated (10-5 Torr) quartz tube and put for heat treatments at 750 and 1150 0C in a single step for…
▽ More
We report synthesis, structural details and transport measurements on Sr4V2O6Fe2As2. Namely the stoichiometric amounts of V2O5 + SrO2 + Sr + 2FeAs are weighed mixed, ground thoroughly and palletized in rectangular form in a glove box in high purity Ar atmosphere. The pellet is further sealed in an evacuated (10-5 Torr) quartz tube and put for heat treatments at 750 and 1150 0C in a single step for 12 and 36 hours respectively. Finally the quartz ampoule is allowed to cool naturally to room temperature. The as synthesized sample is black in color. The compound crystallized in P4/nmm space group with lattice parameters a = b = 3.925A and c = 15.870A. Also seen are some small impurity lines. The compound did not exhibit superconductivity but instead a spin density wave (SDW) like metallic step at around 175 K is seen in R(T) measurements
△ Less
Submitted 23 January, 2012; v1 submitted 21 April, 2009;
originally announced April 2009.
-
Superconductivity at 14K in the Co-doped SmFe0.9Co0.1AsO
Authors:
V. P. S. Awana,
Arpita Vajpayee,
Anand Pal,
Monika Mudgel,
R. S. Meena,
H. Kishan
Abstract:
We report superconductivity in the SmFe0.9Co0.1AsO system being prepared by most easy and versatile single step solid-state reaction route. The parent compound SmFeAsO is non-superconducting but shows the spin density wave (SDW) like antiferromagnetic ordering at around 140K. To destroy the antiferromagnetic ordering and to induce the superconductivity in the parent system, the Fe2+ is substituted…
▽ More
We report superconductivity in the SmFe0.9Co0.1AsO system being prepared by most easy and versatile single step solid-state reaction route. The parent compound SmFeAsO is non-superconducting but shows the spin density wave (SDW) like antiferromagnetic ordering at around 140K. To destroy the antiferromagnetic ordering and to induce the superconductivity in the parent system, the Fe2+ is substituted partially by Co3+. Superconductivity appears in SmFe0.9Co0.1AsO system at around 14K. The Co doping suppresses the SDW anomaly in the parent compound and induces the superconductivity. Magnetization measurements show clearly the onset of superconductivity with Tcdia at 14K. The isothermal magnetization measurements exhibit the lower critical fields (Hc1) to be around 200Oe at 2 K. The bulk superconductivity of the studied SmFe0.9Co0.1AsO sample is further established by open diamagnetic M(H) loops at 2, and 5K. Normal state (above Tc) linear isothermal magnetization M(H) plots excluded presence of any ordered magnetic impurity in the studied compound.
△ Less
Submitted 20 January, 2012; v1 submitted 23 February, 2009;
originally announced February 2009.
-
One-step atmospheric pressure synthesis of the ground state of Fe based LaFeAsO1-d superconductor
Authors:
V. P. S. Awana,
Arpita Vajpayee,
Monika Mudgel,
Anuj Kumar,
R. S. Meena,
Rahul Tripathi,
Shiva Kumar,
R. K. Kotnala,
Hari Kishan
Abstract:
We report an easy and versatile one-step route of synthesis for newly discovered Fe based superconductor LaFeAsO1-d with d = 0.0 to 0.15. Instead of widely used high-pressure-high-temperature (HPHT) synthesis, we applied the normal atmosphere solid-state reaction route. The stoichiometric mixtures of Fe, La2O3, La and As in ratio LaFeAsO1-d with d = 0.0 to 0.15 are sealed in an evacuated quartz…
▽ More
We report an easy and versatile one-step route of synthesis for newly discovered Fe based superconductor LaFeAsO1-d with d = 0.0 to 0.15. Instead of widely used high-pressure-high-temperature (HPHT) synthesis, we applied the normal atmosphere solid-state reaction route. The stoichiometric mixtures of Fe, La2O3, La and As in ratio LaFeAsO1-d with d = 0.0 to 0.15 are sealed in an evacuated quartz tube and further heated at 500, 850 and 1100 0C in Ar for 12, 12 and 33 hours respectively in a single step. The resulting compounds are single phase LaFeAsO crystallized in tetragonal P4/nmm structure. These samples showed the ground state spin density wave (SDW) like metallic behavior below around 150 K. In conclusion the ground state of newly discovered Fe based superconductor is synthesized via an easy one-step solid-state reaction route.
△ Less
Submitted 2 May, 2008;
originally announced May 2008.